Rica - i nostri prodotti

EPOSTUC RP

two component adhesive epoxy for gluing and stuccoing to elevated performances

Characteristics

mix relationship Part To / Part B	1 / 1 (is in weight that in volume)
Aspect of the members mix:	Fluid tizotropico gray
Dissolvents:	Absent
Mechanism of hardening:	Reaction between the two members
Useful time after mix to 20°C:	1 hour
Time of hardening to 20°C	10 hours
Complete hardening to 20°C	2 days
Temperature of application	from +5°C to +40°C
Temperature of exercise:	from -30°C to -100°C
Adhesion to the concrete:	3.8 N/mm2 (breach CLS)

Property and advantages

Facility of application and good spatulable also to thickness of 3-4 cm.
Highest adhesive power, also on humid superficial
Express attainment of excellent mechanical resistances
Optimal resistance to the main chemical agents
The dissolvent absence concurs the use also in little aired atmospheres sluices
Optimal to fill
Elevated impermeability to the water and gases
Dimensional stability and practically null withdrawal

It employs:

glue of elements in concrete, metal, stone, etc
sealing in restructure works.
Anchorage of prisoners
stuccoing of fissures, holes, nest and pulling for quarter-deck
regularization of superficial of structures subject to strong sollicitations chemical-mechanics

Modality of use

The superficial ones must be clean, compact, dry and lacking in oils, and powder.

To accurately stir the two members in the exact relationships, before the use, possibly with mechanical propeller bottoming drill to 250-300 turn/min., avoiding the excessive air.

The mix modelable is completed when the paste introduces one uniform grey coloration. EPOSTUC - RP the easy modelable one also during the hardening; for a perfect finish degree, to damp the tools with water. The application can come carried out to spatula or trowel.

Confection:

EPOSTUC - BP is available in drums from 1,5 kg. (BASES) + 1.5 kg. (HARDENING)

The time of storage, in place dry and protect from ices and heat, is until 12 months. The product must be conserved to temperatures comprised between 4-5 e+35' C.